ZCAT-Z19P

ZCAT-Z19P is generally used in various fields of polyurethane industry. It is recommended to be used for plastic runway, slicone PU, etc. it has better catalytic effect when collocates with bismuth catalyst model BCAT-20BP

TDS Download
Description

Product Name: Organic Bismuth Zinc Catalyst ZCAT-Z19P


Brand Name: Yourun Catalyst, YR Catalyst

 

Typical Properties:

Model

Appearance

Colour  (Fe-Co)

Density

g/cm3 (25℃)

Viscosity

mPa.s (25℃)

Metal Content

Smell

BCAT-20BP

Colorless to yellowish transparent liquid

≤ 3

1.135-1.175

100±50

20±0.5

With special compound smell

ZCAT-Z19P

1.112-1.152

3200±1000

19±0.5


Solubility:Soluble in general polyurethane raw materials.

 

Eco-friendly Characteristic:

It does not contain restricted heavy metals, polycyclic aromatic hydrocarbons, phthalates and other components, and is an environmentally friendly substitute for traditional organotin, mercury, lead and other catalysts.

 

Applications:

It is generally used in various fields of polyurethane industry. It is recommended to be used for plastic runway resin, slicon PU resin, etc. it has better catalytic effect when collocates with bismuth catalyst model BCAT-20BP.

 

Features & Advantage:

  • Organic zinc ZCAT-Z19P, as a polyurethane catalyst with weak catalytic activity, is not used alone in most cases and is used in combination with organic bismuth. The weak catalytic properties of organic zinc make the flow period of materials long after mixing, which is beneficial for construction operations;

  • Organic bismuth BCAT-20BP promotes the NCO/OH reaction, which can to some extent reduce the side reactions between water and NCO groups and reduce the generation of CO2. However, the targeted selectivity for reducing the reaction between isocyanates and water is not as good as that of the Yourun CUCAT series catalyst products;

  • The two models have good compatibility and can be combined in any proportion according to construction requirements, so as to achieve the effect of long operation time and fast post curing.

 

User's Guide:

  • For plastic runway materials, it is recommended to add into polyol (P material) components. It is recommended to add after dehydration and stir evenly;

  • It can also be added during on-site construction, with an appropriate amount added according to the construction environment temperature to achieve the best process effect;

  • The usage amount is related to the formula system, generally ranging from 0.1 to 0.5% of the weight of P material;

  • The viscosity of this product is moderate. If it needs to be diluted, it is recommended to use D40 or other isomeric alkane solvent oils to achieve the best effect. It can also be diluted with polyethers, plasticizers, etc;

  •  It is not recommended to add it to the isocyanate component (material I). If it is must, it is necessary to conduct suitability and storage stability experiments first.

  • Be sure to seal and store immediately after use.

 

Handling & Storage:

Product should be stored in a cool, dry environment away from sunlight, excessive heat and rain.

 

Package: 25kg/200kg in HDPE drum

 

Shelf Life: The unopened shelf life is 18 months from the date of manufacture. 